TECHNICAL INFORMATION

Mechnical Composition

MECHANICAL PROPERTIES

Grade

Tensile
Strength Mpa, (Min)

Yield
Strength
Mpa, (Min)

%Age
Elongation
in 50mm
gauge length min

Hardness (Max)

BHN

Rb

301

515

205

40

217

95

304

515

205

40

201

92

304L

485

170

40

201

92

310S

515

205

40

217

95

316

515

205

40

217

95

316L

485

170

40

217

95

317

515

205

35

217

95

317L

515

205

40

217

95

321

515

205

40

217

95

347

515

205

40

201

92

409

380

170

20

179

88

409M

430

275

20

187

90

410S

415

205

22

183

89

410

450

205

20

217

89

420

700( max )

-

15

217

95

430

450

205

22

183

89

JSL AUS

515

205

40

217

95

JS- 203

515

205

40

217

95

301M

515

205

40

217

95

Nickel Alloy Data

Analyses Analyses Composition
Handelsbezeichung
Designation Comercial
Comercial designation		 C% Co% Cr% Mo% Ni% V% W% Ai% Cu% Nb/Cb Ta% Ti% Fe% Sonstige Autres-Other%
Monel 400 0.12 - - - 65.0 - - - 32.0 - - 1.5 Mn 1.0
Monel 401 0.10 - - - 43.0 - - - 53.0 - - 0.75 Si 0.25; Mn 2.25
Monel 404 0.15 - 52.0-57.0 - - 0.05 rest/bal - - 0.50 Mn 0.10; Si 0.10;S o.024
Monel 502 0.10 - - - 63.0-17.0 - - 2.5-3.5 rest/bal - 0.50 2.0 Mn 1.5;Si 0.5; S 0.010
Monel K 500 0.13 - - - 64.0 - - 2.8 30.0 - 0.6 1.0 Mn 0.8
Monel R 405 0.15 - - - 66.0 - - - 31.0 - - 1.2 Mn 1.0; S 0.04
Hastelloy B 0.10 1.25 0.60 28.0 rest/bal 0.30 - - - - - 5.50 Mn 0.80; Si 0.70
Hastelloy B2 0.02 1.0 1.0 26.0-30.0 rest/bal - - - - - - 2.0 Mn 1.0: Si 0.10
Hastelloy C 0.07 1.25 16.0 17.0 rest/bal 0.30 40 - - - - 5.75 Mn 1.0 :Si 0 0.70
Hastelloy C4 0.015 2.0 14.0-18.0 14.0-17.0 rest/bal - - - - - 0..70 3.0 Mn 1.0 ; Si 0.08
Hastelloy C 276 0.02 2.5 14.0-16.5 15.0-17.0 rest/bal 0.35 3.0-4.5 - - - - 4.0-7.0 Mn 1.0;Si 0.05
Hastelloy F 0.02 1.25 22.0 6.5 rest/bal - 0.50 - - Nb2.10 - 21.0 Mn 1.50;Si 0.50
Hastelloy G 0.05 2.5 21.0-23.5 5.5-7.5 rest/bal - 1.0 - 1.5-2.5 Nb1.75-2.5 - 18.0-21.0 Mn 1.0-2.0;p0.04;Si 1.0;80.03
Hastelloy G-2 0.03 - 23.0-26.0 5.0-7.0 47.0-52.0 - - - 0.70-1.20 - 0.70-1.50 rest/bal Mn 1.0;Si 1.0
Hastelloy N 0.06 0.25 7.0 16.5 rest/bal - 0.20 - 0.10 - - 3.0 Mn 0.40;Si 0.25;B0.01
Hastelloy S 0.02 2.0 15.5 14.5 rest/bal 0.6 1.0 0.20 - - - 3.0 Mn 0.50;Si 0.40;B0.0009;LA 0.02
Hastelloy W 0.06 1.25 5.0 24.5 rest/bal - - - - - - 5.5 Mn 0.050 ; Si 0.50
Hastelloy X 0.10 1.50 22.0 9.0 rest/bal - 0.60 - - - 18.5 - Mn 0.6; Si 0.60
Incoloy 800 0.04 - 21.0 - 32.0 - - 0.3 - - 0.4 45.0 -
Incoloy 800 H 0.08 - 21.0 - 32.0 - - 0.3 - - 0.4 45.0 -
Incoloy 801 0.05 - 20.5 - 32.0 - - - - - 1.1 45.0 -
Incoloy 802 0.35 - 21.0 - 32.0 - - 0.6 - - 0.7 45.0 -
Incoloy 804 0.05 - 29.5 - 41.0 - - 0.3 - - 0.6 25.4 -
Incoloy 805 0.12 - 7.5 0.50 36.0 - - - 0.10 - - rest/bal Mn 0.60;Si 0.50
Incoloy 810 0.25 - 21.0 - 32.0 - - - 0.50 - - rest/bal Mn 0.90; Si 0.80
Incoloy 825 0.04 - 21.0 3.0 42.0 - - - 2.0 - 1.0 30.0 -
Incoloy 825 Cp 0.04 - 21.5 3.0 42.0 - - - 2.2 Nb0.9 - 30.0 -
Incoloy 840 0.08 - 20.0 - 20.0 - - - - - - rest/bal Mn 1.0;Si 1.0
Incoloy 901 0.05 - 12.5 6.0 rest/bal - - 0.15 - - 2.70 34.0 Mn 0.24;Si 0.12;B0.015
Incoloy 901 Mod 0.05 - 12.5 5.80 rest/bal - - - - - 2.9 34.0 Mn 0.09;Si 0.08;B0.015
Incoloy 903 0.02 15.0 - - 38.0 - - 0.7 - Nb 3.0 1.4 41.0 -
Incoloy 904 0.02 14.0 - - 33.0 - - - - - 1.7 50.0 -
Incoloy DS 0.06 - 18.0 - 37.0 - - - - - - 42.0 Mn 1.0; Si 2.3
Incoloy Ma 956 - - 20.0 - - - - 4.5 - - 0.5 74.4 Y2.03 0.5
Incoloy 600 0.05 - 15.5 - 75.0 - - - - - - 8.0 -
Incoloy 601 0.05 - 23.0 - 60.0 - - 1.4 - - - 14.0 -
Incoloy 604 0.04 - 15.8 - rest/bal - - - 0.10 Nb 2.0 - 7.20 Mn 0.20; Si 0.20
Incoloy 610 0.20 - 15.5 - rest/bal - - - 0.50 Nb 1.0 - 9.0 Mn 0.90;Si 2.0
Incoloy 617 0.07 12.5 22.5 9.0 54.0 - - 1.0 - - - - -
Incoloy 625 0.05 - 21.5 9.0 61.0 - - 0.40 - Nb 3.65 0.40 2.5 Mn 0.50; Si 0.50
Incoloy 671 0.05 - 48.0 - 51.0 - - - - - 0.35 - -
Incoloy 700 0.12 28.5 15.0 3.75 46.0 - - 3.0 0.05 - 2.20 0.70 Mn 0.10; Si 0.30
Incoloy 702 0.04 - 15.6 - rest/bal - - 3.4 0.10 - 0.70 0.35 Mn 0.05: Si 0.20
Incoloy 705 0.30 - 15.5 - rest/bal - - - 0.50 - - 8.0 Mn 0.90 ; Si 5.5